Method to prepare defective metal oxides with increased specific capacity

ABSTRACT

Increased lithium capacity of defective oxide materials and methods for preparation are described herein. Point defects may be introduced into a metal oxide to increase its lithium ion capacity. Defective metal oxides can be prepared by heating the metal oxide under O 2 /H 2 O at elevated temperatures. These increased lithium capacity metal oxides may be suitable for use as high specific energy cathodes in lithium metal and lithium ion batteries.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates generally to improved capacity of defective materials and more specifically to the preparation of defective metal oxides for battery cathodes with increased specific energy and improved lithium capacity.

[0003] 2. Discussion of the Background

[0004] The revolution in the portable electronics industry has increased the demand for lightweight, high-energy batteries. Strategies for improving the energy density of batteries include technical challenges such as (1) increasing the voltage difference between the cathode and anode, (2) decreasing the weight of the materials, and (3) increasing the charge-storage capacity of the materials.

[0005] The obstacles to these improvements are often physical. For instance, the lithium (Li) capacity of metal-oxide charge-storage materials is limited because the valence of the metal cations fixes the number of electrons withdrawn from each metal center, as shown for the V₂O₅-cathode half-cell reaction in Eq. 1. Only one electron is consumed when a lithium ion from an electrolyte solution (Li_((sol)) ⁺) inserts into a V₂O₅ cathode and a V⁵⁺ ion is reduced to V⁴⁺ (Eq. 1).

V_(v)+Li_((sol)) ⁺ +e ⁻=V_(v)′+Li_(i) ^(•)  (1)

[0006] Using Kröger-Vink notation, V_(v) designates a V⁵⁺ ion at a vanadium-cation site in the V₂O₅ lattice, and V_(v)′ represents the occupation of the cation site with a V⁴⁺ ion, leaving it effectively 1-negative (′). Li_(i) ^(•) represents a lithium ion that is located in an interstitial site (i) and has an effective 1-positive charge (^(•)). The Li⁺ may actually be associated with an oxygen anion, but this defect is electrically and site equivalent to a lithium interstitial. Kröger-Vink notation, which is used to write equilibrium reactions and mass action equations in defective oxides, is also useful for writing equations for the metal oxides used in batteries, because it demands site and charge balance in addition to chemical balance and includes defects (vacancies, etc.) as chemical species.

[0007] The vanadium cations in bulk V₂O₅ are reduced to an average oxidation state of +4.5 with Li⁺ insertion, because structural constraints allow reduction of only half of the V⁵⁺ ions to V⁴⁺. This physical limitation of 0.5 electron stored per vanadium ion is broken when Li⁺ is inserted into V₂O₅ materials synthesized by sol-gel methods. Up to 2.5 Li⁺ can be inserted per vanadium ion into the amorphous, high surface area, high porosity frameworks of V₂O₅ aerogels and xerogels, resulting in capacities as high as 600 mAh/g. Although Eq. (1) predicts V³⁺ defects should be formed when 3 to 5 equivalents of Li⁺ are inserted into V₂O₅ xerogels and aerogels, X-ray absorption spectroscopy (XAS) studies indicate that only V⁴⁺ and V⁵⁺ ions are present in the fully discharged materials. Raman spectroscopy shows unique vibrational bands in Li—V₂O₅ xerogels, but provides no identification of the mechanism for the additional Li⁺ insertion. Even if the metal-oxide materials become metallic, the charge balance constraints in Eq. 1 still apply.

SUMMARY OF THE INVENTION

[0008] The present invention has been made in view of the above-described problems that need to be solved, and an object of the present invention is therefore to provide a method to improve the lithium capacity of metal oxide materials. Point defects are introduced into a metal oxide to increase its lithium ion capacity.

[0009] Accordingly, it is one object of the present invention to provide a novel method for the preparation of defective metal oxides for battery cathodes with increased capacity.

[0010] It is another object of this invention to provide a method for the preparation, using a heat treatment, of defective metal oxides for battery cathodes with increased capacity.

[0011] It is another object of this invention to provide a method for the preparation, by using a chemical treatment, of defective metal oxides for battery cathodes with increased capacity.

[0012] It is another object of this invention to provide a method for the preparation of defective metal oxides for battery cathodes with increased capacity.

[0013] These and other objects, which will become apparent during the following detailed description, have been achieved by the inventors' discovery that lithium-ion capacity of metal oxides may be controlled via point defects that may be introduced into a metal oxide by:

[0014] (a) applying a mixture of O₂ and H₂O gas to a sufficient amount of a V₂O₅ metal oxide sample at a linear flow rate of about 50-350 cm;

[0015] (b) heating the metal oxide sample at a temperature of about 300-600° C. for a time period of about 6-72 hours; and

[0016] (c) cooling the metal oxide sample.

BRIEF DESCRIPTION OF THE DRAWINGS

[0017] A more complete appreciation of the invention and many of the attendant advantages thereof will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings, wherein:

[0018]FIG. 1 is an illustration of X-ray diffraction (XRD) patterns of V₂O₅ samples as received and after heating under different gas mixtures. The different samples shown are (a) as received, and after heating under (b) O₂, (c) O₂/H₂O, (d) Ar, and (e) Ar/H₂O.

[0019]FIG. 2 is an illustration of charge-discharge profiles of 0.5 mg V₂O₅ electrodes after treatment by heating under different atmospheres (A) first complete charging cycle (10 μA), (B) first complete discharge cycle (10 μA).

[0020]FIG. 3 is a table showing a series of V₂O₅ samples heated under different atmospheres: capacity of 0.5 mg samples at discharge rate of 10 μA, and open-circuit potential (OCP) of the materials before cycling.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0021] Thus, in a first embodiment, the present invention provides for

[0022] (a) applying a mixture of O₂ and H₂O gas to a sufficient amount of a V₂O₅ metal oxide sample at a linear flow rate of about 50-350 cm;

[0023] (b) heating said metal oxide sample at a temperature of about 300-600° C. for a time period of about 6-72 hours; and

[0024] (c) cooling said metal oxide sample.

[0025] Vacancies may be introduced into the vanadium oxide (V₂O₅) lattice during heating under various atmospheric conditions. It is to be understood that “V₂O₅” describes vanadium oxide in which the vanadium is predominantly in the +5 valence state.

[0026] To examine the interaction of Li⁺ with defects in the V₂O₅ lattice, commercially available, anhydrous, bulk V₂O₅ is made defective by conventional heat treatments under O₂, O₂/H₂O, Ar, and Ar/H₂O, and the treated materials are tested for changes in Li capacity relative to the as-received V₂O₅ powder. Although bulk V₂O₅ usually has lower capacity than materials synthesized from sol-gels, it is compositionally uniform and stable, and therefore an ideal standard material.

[0027] A range of defective V₂O₅ materials is prepared by heating commercial V₂O₅ powder (Alfa) under O₂, O₂/H₂O, Ar, and Ar/H₂O. Approximately 1 g of the as-received V₂O₅ powder is loaded into an alumina boat in a 1″ diameter alumina tube under ˜350 ccm flowing O₂, O₂/H₂O, Ar, or Ar/H₂O and heated at 5° C./min to 460° C. After holding at 460° C. for 24 h, the samples are cooled at 5° C./min to room temperature and then stored in sealed vials under ambient air.

[0028] The structure of the V₂O₅ samples is determined via XRD (Rigaku Rotoflex, Cu rotating anode, 50 kV and 150 mA). Powder samples are mounted with double-stick tape on glass slides. Electrodes are prepared by vigorously mixing the V₂O₅ with 13 wt % acetylene black (Alfa), 9 wt % polyvinylidene fluoride (PVDF, Elf Atochem) in an excess of either 2-methyl pentanone (Aldrich) at 60° C. or hexanes (Aldrich) at room temperature. The suspension is added dropwise to a strip of clean Pt foil and heated on a hot plate to remove excess solvent. The amount of material on the foil (0.5 to 1.5 mg) is then adjusted so that the V₂O₅ weight in all samples is within ±2%. After vacuum drying at >150° C. for 12 to 24 h, the electrodes are loaded into an Ar-filled glove box. The V₂O₅/Pt electrodes are tested in a solution of 1 M Li-perchlorate (Aldrich) in distilled propylene carbonate (Aldrich) vs Li metal auxiliary and reference electrodes (Aldrich). The electrodes are charged and discharged between 2 and 4 V vs Li using a potentiostat (PAR 263; M270 software) in galvanostatic mode. The open-circuit potential (OCP) of each electrode is measured after equilibrating for at least 10 min in the Li-propylene carbonate electrolyte. The samples are first charged to 4 V to displace residual protons before discharging to 2 V. Acetylene black and platinum electrodes with no V₂O₅ have negligible capacity when charged and discharged between 2 and 4 V.

[0029] X-ray diffraction shows that the as-received, orange-colored V₂O₅ is crystalline and has the Shcherbinaite structure (ICCD PDF Card # 41-1426). The same phase is measured for the samples heated at 460° C. under O₂, O₂/H₂O, and Ar (FIG. 1), indicating that the long-range structure of the V₂O₅ is not affected by these temperature/atmosphere/time conditions and suggesting that ionic defects have been introduced. All of these samples are also orange-colored after reacting under heat. The XRD pattern of the green-black Ar/H₂O-heated V₂O₅ indicates that it is highly disordered to amorphous and has only a trace of the Shcherbinaite structure. Additional peaks are measured in the Ar/H₂O-heated V₂O₅ but these diffraction peaks cannot be matched to a single vanadium-oxide or hydrous vanadium-oxide phase.

[0030] The Li capacity of V₂O₅ powder is significantly affected by the heating conditions. FIG. 2 shows a series of electrodes that contain 0.5 mg of V₂O₅ that are charged and discharged at 10 μA (20 μA/mg); the Li capacity results are summarized in Table I. Under these charging and discharging conditions, the capacity of the Ar/H₂O-heated V₂O₅ is 72 mA-h/g (±4%), which is almost 58% lower than the capacity of the as-received V₂O₅ (172 mA-h/g). The capacity of the O₂/H₂O-heated V₂O₅ is 212 mA-h/g, or 22% greater than the capacity of the as-received V₂O₅. The capacities of the Ar-heated and O₂-heated V₂O₅ are 8% and 25% lower than that of the as-received V₂O₅, respectively. The profiles of the charge and discharge curves are identical for the samples heated under O₂, O₂/H₂O, and Ar versus the as-received V₂O₅, however the time (or capacity) of each charge and discharge potential step varies.

[0031] The values measured for the Li capacities vary between different batches of electrodes probably due to variations in the sample weights (or electrode thicknesses) and drying conditions. However, the same trends are observed. Also, the differences in the capacities of the V₂O₅ materials are lessened as they are discharged at higher rates (up to 100 μA/mg). The capacity of all of the V₂O₅ powders fades by 1 to 3% after each cycle. The acetylene black and platinum make negligible contributions to the results.

[0032] In comparison to the as-received V₂O₅, the OCPs of the O₂- and Ar-heated V₂O₅ are ˜65 mV higher, the O₂/H₂O-heated V₂O₅ is 50 mV higher, and the Ar/H₂O-heated material is only ˜5 mV higher. The OCP values vary between electrode batches, but the trend remains the same.

[0033] Heating bulk V₂O₅ under O₂, O₂/H₂O, and Ar causes no change to the long-range structure of the metal oxide, but it significantly affects the V₂O₅ lithium capacity. Under the O₂, Ar, and Ar/H₂O heating steps, the Li capacity is decreased. The lithium capacity is increased for the samples heated under O₂/H₂O. Since the long-range structure does not change, this suggests that local ionic defects introduced by the O₂/H₂O heat treatment, such as cation vacancies, are affecting the lithium capacity of the metal oxide.

[0034] The V₂O₅ that is heated under Ar/H₂O has ˜60% decrease in Li capacity versus the as-received material, but it also undergoes a phase transformation to a highly disordered, hydrous structure during temperature/atmosphere treatment. These results support the supposition that the high Li capacity of V₂O₅ materials prepared by sol-gel methods is not just due to their hydrous, highly disordered structure, but rather to another effect such as ionic defects.

[0035] The change in the OCPs of the heated V₂O₅ materials indicates that they are thermodynamically different from the as-received material. It is suggested that other metal oxides behave similarly with O₂/H₂O heating. Examples of metal oxides include vanadium oxide, manganese oxide, nickel oxide, cobalt oxide, and iron oxide. The metal oxide can be in its stoichiometric or non-stoichiometric form. The metal oxide can be doped with a transition metal. Additionally, the lithiated form of the metal oxide can be used.

[0036] Hydrogen ions (i.e., protons and hydride ions) usually behave similarly to lithium ions. This approach is applicable to other battery systems using metal oxides, such as alkaline and metal hydride batteries. 

We claim:
 1. A process for introducing defects into a metal oxide, said process comprising the steps of: applying a gas to a sufficient amount of a metal oxide sample to increase the specific energy; heating said metal oxide sample; and cooling said metal oxide sample.
 2. The process as in claim 1, further comprising the step of: maintaining said heating step at a temperature of from about 300 to about 600° C.
 3. The process as in claim 2, wherein said heating step is maintained from about 6 to about 72 hours.
 4. The process as in claim 1, wherein said gas is applied to said metal oxide sample at a linear flow rate of at least about 50 cm.
 5. The process as in claim 1, wherein said heating step is from about 2 to about 20° C./min up to about 460° C.
 6. The process as in claim 5, further comprising the step of: maintaining said temperature of about 460° C. for 24 hours.
 7. The process as in claim 1, wherein said cooling is from about 2 to about 20° C./min until ambient air temperature is achieved.
 8. The process as in claim 1, wherein said gas is a mixture of O₂ and H₂O_((g)).
 9. The process as in claim 1, wherein said metal oxide sample is V₂O₅.
 10. The process as in claim 1, wherein said sufficient amount comprises metal oxide comprising a surface area of about 1-10 square meters.
 11. A process for preparing a metal oxide for a battery cathode with increased capacity, said process comprising: applying a mixture of O₂ and H₂O gas to a sufficient amount of a V₂O₅ metal oxide sample at a linear flow rate of about 50-350 cm; heating said metal oxide sample at a temperature of from about 300 to about 600° C. for a time period of from about 6 to about 72 hours; and cooling said metal oxide sample.
 12. The product of the process as in claim
 11. 13. Vanadium oxide with increased ionic defect concentration.
 14. A metal oxide with increased ionic defect concentration.
 15. A metal oxide with increased lithium ion capacity.
 16. A metal oxide with increased specific capacity. 